Cold asphalt mix is produced by mixing unheated mineral aggregate with either emulsified bitumen or foamed bitumen. Unlike hot mix asphalt (HMA), cold asphalt mix does not require any heating of aggregate which makes it economical and relatively pollution-free (no objectionable fumes or odours). Production of cold asphalt mix does not require high investment in equipment, which makes it economical. It is also suitable for use in remote areas. Cold asphalt mixes can be used both for initial construction (100% virgin mixes) and for recycling of asphalt pavements.
Cold asphalt mixes do have some limitations. These mixes should not be used when ambient temperatures under 10°C are expected during construction. Cold asphalt mixes are typically suitable for light to medium trafficked roads when used in base and surface courses. Since their structural strength is relatively lower than that of HMA, the pavement structure should be designed properly.
Primarily two types of virgin cold asphalt mixes are used: Dense graded and Open graded. Dense graded mixes are continuously graded from the maximum aggregate size down to material passing 0.075 mm sieve size. Open graded mixes usually lack material passing 2.67 mm sieve and have high air voids.
Slurry seal and microsurfacing can also be considered cold mixes although used as surface treatment. The slurry seal consists of a mixture of mineral aggregate (mostly fine aggregate), slow setting cationic bitumen emulsion, water and additives (if needed) proportioned, mixed and uniformly spread over a prepared surface. The mixture is free flowing like freshly made cement concrete and is applied with a self-propelled slurry seal machine. Microsurfacing is like slurry seal, the primary difference being the former uses a modified (polymer or rubber latex) bitumen emulsion. Untitled photographs in this article show application of microsurfacing.